精密不锈钢带


  首页         精密不锈钢带 

日本牌号

状态中国牌号化学成份(%)导电率(IACS)抗拉强度(N/mm2)伸长率(%)硬度(HV)屈服伏强度
(N/mm2)
SUS3011/4HSUS301C<0.15 Si<1.0 Mn<2.0 S<0.03 Cr:16.0-18.0 Ni:6.0-8.0   Fe:余量  \≥520≥18%250-310205min
SUS301H/2SUS301C<0.15 Si<1.0 Mn<2.0 S<0.03 Cr:16.0-18.0 Ni:6.0-8.0   Fe:余量\≥930≥15%310-370510min
SUS3013/4HSUS301C<0.15 Si<1.0 Mn<2.0 S<0.03 Cr:16.0-18.0 Ni:6.0-8.0   Fe:余量\≥1130≥10%370-430745min
SUS301HSUS301C<0.15 Si<1.0 Mn<2.0 S<0.03 Cr:16.0-18.0 Ni:6.0-8.0   Fe:余量\≥1320≥3%430-4901030min
SUS301EHSUS301C<0.15 Si<1.0 Mn<2.0 S<0.03 Cr:16.0-18.0 Ni:6.0-8.0   Fe:余量\≥1570≥1%490-5301275min
SUS304ANN
C<0.08 Si<1 Mn<2 P<0.045 Ni8-10.5 Cr:18-20 S<0.03   Fe余量\≥521≥41%160-200203min
SUS3041/4H
C<0.08   Si<1 Mn<2 P<0.045 Ni8-10.5 Cr:18-20 S<0.03 Fe余量\≥603≥20%200-250250min
SUS304H/2
C<0.08 Si<1 Mn<2 P<0.045 Ni8-10.5 Cr:18-20 S<0.03   Fe余量\≥780≥15250-310470min
SUS3043/4H
C<0.08 Si<1 Mn<2 P<0.045 Ni8-10.5 Cr:18-20 S<0.03   Fe余量\≥931≥10310-370670min
SUS304H
C<0.08 Si<1 Mn<2 P<0.045 Ni8-10.5 Cr:18-20 S<0.03   Fe余量\≥1130≥5370-430881min

SUS430-1D

SUS430-1BD

软态
C<0.12 Si<0.75 Mn<1 P<0.04  Cr:16-18 S<0.03   Fe余量

/160-180/
1/2H
C<0.12 Si<0.75 Mn<1 P<0.04  Cr:16-18 S<0.03   Fe余量\540-6506.5-10180-230/
BA
C<0.12 Si<0.75 Mn<1 P<0.04  Cr:16-18 S<0.03   Fe余量
47030140min/

 2.   不锈钢的物理特性


品种杨氏模量密度比热热传导率比抗阻热膨胀系数
SUS301193 
7.930.516.37216.9
SUS3041937.930.516.37217.3
SUS4302007.70.4626.46010.4
SUS3051937.930.516.37217.3
SUS3161937.930.516.37217.3